Home › Engineering › Nylon CF

Nylon CF print settings

Nylon-CF combines nylon toughness with carbon-fiber stiffness for demanding parts. Recommended baseline: 265°C hotend, 90°C bed, 0% part-cooling fan. Pick your printer below for a tuned profile.

⚡ Quick answer: Nylon CF prints best around 265°C hotend and 90°C bed. Abrasive and hygroscopic — a hardened nozzle and thorough drying are essential.

Nylon CF settings by printer

Printer	Hotend	Bed	Speed	Fit
Anycubic Kobra S1	265°C	90°C	98 mm/s	✅
Anycubic Kobra 2	265°C	90°C	55 mm/s	⛔
Anycubic Kobra 2 Pro	265°C	90°C	78 mm/s	⚠️
Bambu Lab A1	265°C	90°C	98 mm/s	⚠️
Bambu Lab A1 mini	265°C	90°C	98 mm/s	⚠️
Bambu Lab H2D	265°C	90°C	130 mm/s	✅
Bambu Lab P1P	265°C	90°C	117 mm/s	⚠️
Bambu Lab P1S	265°C	90°C	117 mm/s	✅
Bambu Lab X1 Carbon	265°C	90°C	130 mm/s	✅
Elegoo Centauri Carbon	265°C	90°C	117 mm/s	✅
Creality K1	265°C	90°C	117 mm/s	✅
Creality K1 Max	265°C	90°C	117 mm/s	✅
Creality K1C	265°C	90°C	117 mm/s	✅
Creality Ender 3	265°C	90°C	33 mm/s	⛔
Creality Ender 3 Pro	265°C	90°C	33 mm/s	⛔
Creality Ender 3 S1	265°C	90°C	52 mm/s	⛔
Creality Ender 3 S1 Pro	265°C	90°C	59 mm/s	⚠️
Creality Ender 3 V2	265°C	90°C	39 mm/s	⛔
Creality Ender 3 V3	265°C	90°C	78 mm/s	⚠️
Creality Ender 3 V3 KE	265°C	90°C	78 mm/s	⚠️
Creality Ender 3 V3 SE	265°C	90°C	59 mm/s	⛔
Creality Ender 5 S1	265°C	90°C	78 mm/s	✅
Flashforge Adventurer 5M	265°C	90°C	98 mm/s	⚠️
Elegoo Neptune 4	265°C	90°C	78 mm/s	⚠️
Elegoo Neptune 4 Max	265°C	90°C	78 mm/s	⚠️
Elegoo Neptune 4 Pro	265°C	90°C	78 mm/s	⚠️
Prusa MINI+	265°C	90°C	65 mm/s	⚠️
Prusa MK3S+	265°C	90°C	65 mm/s	⚠️
Prusa MK4	265°C	90°C	91 mm/s	⚠️
Prusa MK4S	265°C	90°C	111 mm/s	⚠️
QIDI X-Plus 3	265°C	90°C	117 mm/s	✅
Sovol SV06	265°C	90°C	59 mm/s	⚠️
Sovol SV07	265°C	90°C	98 mm/s	⚠️
Voron 2.4	265°C	90°C	130 mm/s	✅

Sources & how we tuned this

These settings are community-tested starting points, cross-checked against manufacturer guidance and trusted material references:

Last verified: 2026-07-17. Always run a temperature tower and a small calibration print for your exact spool.